Interconnect structure and method for forming the same

ABSTRACT

A interconnect structure includes a conductive layer formed in a dielectric layer. An adhesion layer is formed between the dielectric layer and a substrate. The adhesion layer has a carbon content ratio greater than a carbon content ratio of the dielectric layer.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims priority of U.S. Provisional Patent Application No. 61/617,530, filed on Mar. 29, 2012, which is incorporated herein by reference in its entirety.

TECHNICAL FIELD

The present disclosure relates to semiconductor devices and particularly to copper interconnects and methods for their fabrication.

BACKGROUND

Semiconductor devices are used in a variety of electronic applications, such as personal computers, cell phones, digital cameras, and other electronic equipment. As technology has progressed, the demand for smaller semiconductor devices with improved performance has increased. As feature densities in the semiconductor devices increase, the widths of the conductive lines, and the spacing between the conductive lines of back-end of line (BEOL) interconnect structures in the semiconductor devices also need to be scaled down.

Several approaches have been implemented in order to meet these demands. As the widths of the conductive lines reduce, the spacing between two successive layers with conductive lines also reduces. The reduced spacing may therefore increase resistance-capacitance (RC) time delay. To reduce the RC time delay, low dielectric constant (low-k) materials are being used as insulating materials, and copper is replacing aluminum for interconnect structures. Advantages of using copper for semiconductor device interconnects include abilities to operate faster and manufacture thinner conductive lines because copper has lower resistivity and increased electromigration resistance compared to aluminum. Combining copper interconnects with low-k dielectric materials increases interconnect speed by reducing the RC time delay, for example.

Copper interconnects are often formed using damascene processes rather than by direct etching. Damascene processes are typically either single or dual damascene, which include forming openings by patterning and etching inter-metal dielectric (IMD) layers and filling the openings with copper. However, there are some challenges in the copper damascene structure, such as adhesion issues between the low-k dielectric material and the underlying layer. The adhesion issues may cause film cracking and/or peeling and, therefore, result in device package qualification failure.

BRIEF DESCRIPTION OF THE DRAWING

The present disclosure is best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale and are used for illustration purposes only. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 is a flow chart of a method for fabricating an integrated circuit device according to an embodiment of the present disclosure.

FIGS. 2-7 are cross-sectional views of an integrated circuit device during various fabrication stages according to the method of FIG. 1 according to an embodiment of the present disclosure.

DETAILED DESCRIPTION

It is understood that the following disclosure provides many different embodiments, or examples, for implementing different features of the disclosure. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

With reference to FIGS. 1 and 2-7, a method 100 and a semiconductor device 200 are collectively described below. The semiconductor device 200 illustrates an integrated circuit, or portion thereof, that can comprise memory cells and/or logic circuits. The semiconductor device 200 can include passive components such as resistors, capacitors, inductors, and/or fuses; and active components, such as P-channel field effect transistors (PFETs), N-channel field effect transistors (NFETs), metal-oxide-semiconductor field effect transistors (MOSFETs), complementary metal-oxide-semiconductor transistors (CMOSs), high voltage transistors, and/or high frequency transistors, other suitable components, and/or combinations thereof. It is understood that additional steps can be performed before, during, and/or after the method 100, and some of the steps described below can be replaced or eliminated, for additional embodiments of the method. It is further understood that additional features can be added in the semiconductor device 200, and some of the features described below can be replaced or eliminated, for additional embodiments of the semiconductor device 200.

Referring to FIGS. 1 and 2, the method 100 begins at step 102, wherein a first etch stop layer (ESL) 220 is formed over a substrate 210. In the present embodiment, the substrate 210 is a semiconductor substrate comprising silicon. In some alternative embodiments, the substrate 210 comprises an elementary semiconductor including silicon and/or germanium in crystal; a compound semiconductor including silicon carbide, gallium arsenide, gallium phosphide, indium phosphide, indium arsenide, and/or indium antimonide; an alloy semiconductor including SiGe, GaAsP, AlInAs, AlGaAs, GaInAs, GaInP, and/or GaInAsP; or combinations thereof. The alloy semiconductor substrate may have a gradient SiGe feature in which the Si and Ge composition change from one ratio at one location to another ratio at another location of the gradient SiGe feature. The alloy SiGe may be formed over a silicon substrate. The SiGe substrate may be strained. Furthermore, the semiconductor substrate may be a semiconductor on insulator (SOI). In some embodiments, the semiconductor substrate may include a doped epitaxial layer. In other embodiments, the silicon substrate may include a multilayer compound semiconductor structure.

The substrate 210 may include various doped regions depending on design requirements (e.g., p-type wells or n-type wells). The doped regions may be doped with p-type dopants, such as boron or BF₂; n-type dopants, such as phosphorus or arsenic; or a combination thereof. The doped regions may be formed directly in the substrate 210, in a P-well structure, in an N-well structure, in a dual-well structure, or using a raised structure. The semiconductor device 200 may include a P-channel Field Effect Transistor (PFET) device and/or an N-channel Field Effect Transistor (NFET) device. Thus, the substrate 210 may include various doped regions configured for the PFET device and/or the NFET device.

The first etch stop layer 220 for controlling the end point during subsequent etching processes is deposited on the above-described substrate 210. In some embodiments, the first etch stop layer 220 comprises a material including C, Si, N, or H. In some embodiments, the first etch stop layer 220 is formed of silicon oxide, silicon nitride, silicon carbide, silicon oxynitride, or combinations thereof. In some embodiments, the first etch stop layer 220 has a thickness of about 10 angstroms to about 1000 angstroms. In some embodiments, the first etch stop layer 220 is formed through any of a variety of deposition techniques, including, low-pressure chemical vapor deposition (LPCVD), atmospheric-pressure chemical vapor deposition (APCVD), plasma-enhanced chemical vapor deposition (PECVD), physical vapor deposition (PVD), sputtering, and future-developed deposition procedures. In some alternative embodiments, the first etch stop layer 220 is formed by a thermal process. In some embodiments, the first etch stop layer 220 having a thickness ranges from about 100 Angstroms to about 300 Angstroms.

Referring to FIGS. 1 and 3, the method 100 continues with step 104 in which a first adhesion layer 230 is formed over the first etch stop layer 220. In some embodiments, the first adhesion layer 230 includes SiOx-containing material, SiCN-containing material, SiON-containing material, or combinations thereof. In some embodiments, the first adhesion layer 230 is formed using LPCVD process, APCVD process, PECVD process, PVD process, sputtering, or future-developed deposition procedures. In some alternative embodiments, the first adhesion layer 230 is formed using a thermal process. In the present embodiment, the first adhesion layer 230 is tetraethoxysilane (TEOS). In some embodiments, the first adhesion layer 230 having a thickness ranges from about 100 Angstroms to about 400 Angstroms.

Referring to FIGS. 1 and 4, the method 100 continues with step 106 in which a second adhesion layer 240 is formed over the first adhesion layer 230. In some embodiments, the second adhesion layer 240 is formed using LPCVD process, APCVD process, PECVD process, PVD process, sputtering, or future-developed deposition procedures. In some alternative embodiments, the second adhesion layer 240 is formed using a thermal process. In some embodiments, the second adhesion layer 240 comprises a material including Si, C, O, or H. In some embodiments, the second adhesion layer 240 is a C-containing layer with a carbon content (C content) ratio in the base composition being greater than 13 at % (atomic percent). In some alternative embodiments, the second adhesion layer 240 is a C-containing layer with C content ratio in the base composition ranging from about 15 at % to about 30 at %. In some embodiments, the second adhesion layer 240 having a thickness ranges from about 5 Angstroms to about 300 Angstroms.

Still referring to FIGS. 1 and 4, the method 100 continues with step 108 in which a dielectric layer 250 is formed over the second adhesion layer 240. The dielectric layer 250 may be a single layer or a multi-layered structure. In some embodiments, the dielectric layer 250 is formed using CVD process, such as PECVD process, LPCVD process, or ALD process. In some embodiments, the dielectric layer 250 comprises a material including Si, C, O, or H. In some embodiments, the dielectric layer 250 comprises elements same as to the second adhesion layer 240 but with a C content ratio less than the C content ratio of the second adhesion layer 240. In some embodiments, the dielectric layer 250 is a C-containing layer with a C content ratio less than 13 at %. In some alternative embodiments, the dielectric layer 250 is a C-containing layer with a C content ratio ranging from about 10 at % and to 13 at %. In some embodiments, the dielectric layer 250 having a thickness ranges from about 300 Angstroms to about 2500 Angstroms.

In some embodiments, the second adhesion layer 240 and the dielectric layer 250 are continuously formed by PECVD. In some embodiments, the second adhesion layer 240 and the dielectric layer 250 use at least one precursor, such as tetramethylcyclotetrasiloxane (TMCTS), octamethylcyclotetrasiloxane (OMCTS), diethoxymethylsilane (DEMS), diethoxyldimethylsilane (DEDMS) and other related cyclic and non-cyclic silanes and siloxanes. In some embodiments, the precursor may be used in conjunction with an inert gas such as He or Ar and/or a reactant gas such as H₂O, O₂, and/or CO₂. In some embodiments, the second adhesion layer 240 and the dielectric layer 250 are continuously formed by PECVD with the same precursor and inert gas. In some embodiments, the second adhesion layer 240 and the dielectric layer 250 are continuously formed by PECVD with the same precursor and inert gas, but with different flow rates of the inert gas and/or different RF powers. In some embodiments, a flow rate of the inert gas for forming the second adhesion layer 240 is greater than a flow rate of the inert gas for forming the dielectric layer 250. In some alternative embodiments, the second adhesion layer 240 is formed using a RF power greater than a RF power for forming the dielectric layer 250. In at least one embodiment, a flow rate of an inert gas for forming the second adhesion layer 240 is greater than a flow rate of the inert gas for forming the dielectric layer 250 and a RF power for forming the second adhesion layer 240 is greater than a RF power for forming the dielectric layer 250.

In some embodiments, the dielectric layer 250 is a low dielectric constant (low-k) layer having a dielectric constant of less than 3.0 and functions as an inter-metal dielectric (IMD) layer. In some embodiments, the dielectric layer 250 is a low-k layer having a dielectric constant ranging from about 2.5 to about 2.8. A wide variety of low-k materials may be employed in accordance with embodiments, for example, spin-on inorganic dielectrics, spin-on organic dielectrics, porous dielectric materials, organic polymer, organic silica glass, SiOF series material (FSG), hydrogen silsesquioxane (HSQ) series material, methyl silsesquioxane (MSQ) series material, or porous organic series material.

In some embodiments, the second adhesion layer 240 has a dielectric constant substantially the same as the dielectric constant of the dielectric layer 250. In some alternative embodiments, the second adhesion layer 240 has a dielectric constant slightly greater than the dielectric constant of the dielectric layer 250, e.g., the different of dielectric constants is less than 2%. In some embodiments, the second adhesion layer 240 functions as an adhesion promotion layer to improve adhesion between the dielectric layer 250 and the first adhesion layer 230. Measured adhesion values that can be obtained by using the second adhesion layer 240 are about 14 J/m² or greater. The measured adhesion values are higher than those in which no further adhesion layer is present between the dielectric layer 250 and the first adhesion layer 230 for about 7% or greater.

Referring to FIGS. 1 and 5, the method 100 continues with step 110 in which an opening 260 is formed in the dielectric layer 250. In some embodiments, the opening 260 is formed through the dielectric layer 250, the second adhesion layer 240, the first adhesion layer 230, and the first etch stop layer 220. In some embodiments, the opening 260 is a dual damascene opening including an upper trench section 260 a and a lower via-hole section 260 b to define a contact region. Although the embodiments illustrate dual damascene opening in the dielectric layer 250, the method disclosed in the present application is applicable for an embodiment having single damascene openings in the IMD layer. In dual damascene techniques including a “via-first” patterning method or a “trench-first” patterning method, the upper trench section 260 a and the lower via-hole section 260 b may be formed using a typical lithographic with masking technologies and anisotropic etch operation (e.g. plasma etching or reactive ion etching). A bottom etch stop layer, a middle etch stop layer, a polish stop layer, or an anti-reflective coating (ARC) layer may be optionally deposited on or intermediately in the dielectric layer 250, providing a clear indicator of when to end a particular etching process.

Referring to FIGS. 1 and 6, the method 100 continues with step 112 in which a conductor 270 is formed in the opening 260. In some embodiments, the conductor 270 is formed by a deposition process, e.g., electro-chemical plating (ECP). In some embodiments, the conductor 270 contains at least one main metal element, e.g., copper (Cu). In some alternative embodiments, the conductor 270 further contains an additive metal element different from the main metal element, such as aluminum.

Still referring to FIG. 6, a barrier layer (not shown) may be deposited to line the sidewalls the openings 260 before forming the conductor 270. In some embodiment, the barrier layer includes Ti, TiN, Ta, TaN, other proper material, or combinations thereof. A conductive seed layer (not shown) may be further formed over the barrier layer before forming the conductor 270. In at least one embodiment, the conductive seed layer is a metal alloy layer containing at least a main metal element, e.g., copper (Cu). In at least one embodiment, the conductive seed layer is formed by using PVD, CVD, PECVD, LPCVD, or other well-known deposition techniques. A chemical mechanical polishing (CMP) process may be performed after the formation of the conductor 270 to remove the excess portions of the conductor 270 over the dielectric layer 250, thus exposing the top surface of the dielectric layer 250 and achieving a planarized surface.

Referring to FIGS. 1 and 7, the method 100 continues with step 114 in which a second etch stop layer 280 is formed on the above-described planarized surface. The second etch stop layer 280 may control the end point during subsequent etching processes. The second etch stop layer 280 may be formed of silicon oxide, silicon nitride, silicon carbide, silicon oxynitride, or combinations thereof, with a thickness of about 10 angstroms to about 1000 angstroms, which may be formed through any of a variety of deposition techniques, including, LPCVD, APCVD, PECVD, PVD, sputtering, and future-developed deposition procedures.

In summary, the disclosed methods and integrated circuit devices result in improved device performance, including but not limited to, improved adhesion between the IMD layer and the underlying layer, and thus the peeling issue can be suppressed. Further, it can improve package capabilities by preventing from peeling during packaging process.

In at least one embodiment, a device comprises a substrate, an adhesion layer having a first carbon content ratio and over the substrate, a dielectric layer having a second carbon content ratio and over the adhesion layer, and a conductor in the dielectric layer. The first carbon content ratio is greater than the second carbon content ratio.

In another embodiment, a semiconductor device comprises a semiconductor substrate, a first adhesion layer over the semiconductor substrate, a second adhesion layer over the first adhesion layer, a low-k dielectric layer over the second adhesion layer, and a conductor in the dielectric layer, the second adhesion layer, and the first adhesion layer. The second adhesion layer and the low-k dielectric comprise C, Si, O elements. An atomic percent of C in the low-k dielectric layer is less than an atomic percent of C in the second adhesion layer.

In still another embodiment, a method comprises forming a first adhesion layer over a substrate, forming a second adhesion layer over the first adhesion layer, forming a low-k dielectric layer over the second adhesion layer, forming an opening in the dielectric layer, the second adhesion layer, and the first adhesion layer, and forming a conductor in the opening. The second adhesion layer is formed using an inert gas with a first flow rate under a first RF power. The low-k dielectric layer is formed using the inert gas with a second flow rate under a second RF power. The second flow rate is different from the first flow rate or the second RF power is different from the first RF power.

Although the embodiments have been described, it is not intended to limit the invention to the precise embodiments disclosed herein. Those skilled in this technology can still make various alterations and modifications without departing from the scope and spirit of this invention. Therefore, the scope of the present invention shall be defined and protected by the following claims and their equivalents. 

What is claimed is:
 1. A device, comprising: a substrate; an adhesion layer over the substrate, the adhesion layer having a first carbon content ratio; a dielectric layer over the adhesion layer, the dielectric layer having a second carbon content ratio, and the first carbon content ratio being greater than the second carbon content ratio; and a conductor in the dielectric layer.
 2. The device of claim 1, wherein the first carbon content ratio is greater than 13 at % (atomic percent).
 3. The device of claim 1, wherein the first carbon content ratio ranges from about 15 at % to about 30 at %.
 4. The device of claim 1, wherein the second carbon content ratio is less than 13 at %.
 5. The device of claim 1, wherein the second carbon content ratio ranges from about 10 at % to about 13 at %.
 6. The device of claim 1, further comprising a SiOx-containing layer, a SiCN-containing layer, or a SiON-containing layer under the adhesion layer.
 7. The device of claim 6, further comprising a first etch stop layer positioned between the substrate and the SiOx-containing layer, the SiCN-containing layer, or the SiON-containing layer.
 8. The device of claim 1, wherein an adhesion strength between the adhesion layer and the SiOx-containing layer, the SiCN-containing layer, or the SiON-containing layer is about 14 J/m² or greater.
 9. The device of claim 1, further comprising a second etch stop layer over the dielectric layer and the conductor.
 10. The device of claim 1, wherein a difference between a dielectric constant of the dielectric layer and a dielectric constant of the adhesion layer is less than about 2%.
 11. The device of claim 1, wherein the dielectric layer having a thickness ranges from about 5 Angstroms to about 300 Angstroms.
 12. A semiconductor device, comprising: a semiconductor substrate; a first adhesion layer over the semiconductor substrate; a second adhesion layer over the first adhesion layer, wherein the second adhesion layer comprises C, Si, or O; a low-k dielectric layer over the second adhesion layer, wherein the low-k dielectric layer comprises C, Si, or O, wherein an atomic percent of C in the low-k dielectric layer is less than an atomic percent of C in the second adhesion layer; and a conductor in the dielectric layer, the second adhesion layer, and the first adhesion layer.
 13. The semiconductor device of claim 12, wherein the atomic percent of C in the low-k dielectric layer ranges from about 10 at % to about 13 at %.
 14. The semiconductor device of claim 12, wherein the atomic percent of C in the second adhesion layer ranges from about 15 at % to about 30 at %.
 15. The semiconductor device of claim 12, wherein the second adhesion layer has a dielectric constant substantially the same as a dielectric constant of the low-k dielectric layer.
 16. The semiconductor device of claim 12, wherein the second adhesion layer has a dielectric constant ranges from about 2.5 to about 2.8.
 17. The semiconductor device of claim 12, wherein an adhesion strength between the first adhesion layer and the second adhesion layer is equal to or greater than about 14 J/m².
 18. A method, comprising: forming a first adhesion layer over a substrate; forming a second adhesion layer over the first adhesion layer, wherein the second adhesion layer is formed using an inert gas with a first flow rate under a first RF power; forming a low-k dielectric layer over the second adhesion layer, wherein the low-k dielectric layer is formed using the inert gas with a second flow rate under a second RF power under at least one of the following two conditions: 1) the second flow rate is different from the first flow rate; and 2) the second RF power is different from the first RF power; forming an opening in the dielectric layer, the second adhesion layer, and the first adhesion layer; and forming a conductor in the opening.
 19. The method of claim 18, wherein the second flow rate is greater than the first flow rate.
 20. The method of claim 18, wherein the second RF power is greater than the first RF power. 